[Sell]RTV2 Silicone Rubber for Moldmaking

PDF: [Sell]RTV2 Silicone Rubber for Moldmaking PDF
Contact Person: Nicole
Telephone: 8676982693920
Address: No.3, Chuang Ye 2nd Rd., He Lu Industrial Zone, Huang Jiang
Region: China
Category: Rubber & Plastics / Rubber Raw Materials
Link Tool: China Rubber & Plastics - China Rubber Raw Materials
View More: [All] [Buy] [Sell] [Cooperation]
Post Time: 2013-03-25T22:10:38+00:00
DESCRIPTION

MC RTV2 mold making Silicone rubber is a two-component material, and the silicone rubber includes Part A base silicone and Part B CA30 curing agent. The Part A base silicone and Part B curing agent can cure at room temperature by a condensation reaction. These silicone materials can be cast into the cured silicone mold: plaster, polyurethane, PU, GRC, cement, resin, polyester, wax etc...

FEATURES

1. Good flow ability and long working time
2. Medium hardness
3. High tear and tensile strength
4. Easy de-mould from complex replica parts
5. Acid and alkali-resistance
6. Low linear shrinkage

APPLICATIONS

MC RTV2 Silicone rubber series are suited for reproduction of cement molding, concrete stones, artificial stones, plaster molding, figures, art objects, decoration molding, GRC products, gypsum products, resin products, PU molds. Etc.


Item RTV 2024
Color off-white
Curing agent CA30
Mixing ratio 100:2
Mixed viscosity 20000-21000 cps
Working time 90-120 mins
Curing time 10-12 Hours
Hardness 24Shore A
Tear Strength 35 N/mm
Tensile Strength 4.7 Mpa
Shrinkage ≤0.3%
Elongation at break 544%
Relative density 1.1-1.15 g/cm3


Instruction for making RTV-2 silicone rubber mold

1. Preparing

The surface of the original objects should be clean and free of loose material. If your products have thin flower patterns, and especially have porous substrates, please use a suitable mold release agent such as soap water, detergent, Vaseline or petroleum jelly.

2. Mixing
Please weigh Part A silicone base and part B CA30 Curing Agent with ratio of 100:2 into a clean container. Stir Part A base silicone thoroughly before use, then Mix Part A and Part B evenly until the curing agent completely dispersed in the silicone base. Manual or mechanical mixture can be used, but do not last much time or allow the temperature to exceed 35℃ (95℉).it’s suitable to mix small quantities to ensure thorough mixture of silicone base and curing agent.
Note: It is strongly recommended that entrapped air be removed in a vacuum chamber, allowing the mixture to completely expand and then collapse. After a further 1 to 2 minutes under vacuum, the mixture should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

3. Pouring and curing
Pour the mixed Part A base silicone and CA-30 curing agent as soon as possible onto the original object, avoiding air entrapment. The catalyzed material will cure to a flexible rubber within 6 hours (or faster by different mixing ratio or room temperature), we advice you de-mold after 24 hours, it is will improve the replicate times of silicone mold.

STORAGE
When the silicone rubber is stored at or below 30 ℃ (85 ℉) in the original unopened containers, RTV2 Silicone Base and CA30 Curing agent have a usable life of 12 months from the date of production. After 12 months, please use a stirring mill to stir the Part A silicone for some minutes, then the silicone can be use again, without any influence to the characteristics.